Catalytic hydrogenation of fluoroolefins, alpha- alumina supported palladium compositions and their use as hydrogenation catalysts

ABSTRACT

A hydrogenation process is disclosed. The process involves reacting a fluoroolefin with H2 in a reaction zone in the presence of a palladium catalyst to produce a hydrofluoroalkane product, wherein the palladium catalyst comprises palladium supported on a carrier wherein the palladium concentration is from about 0.001 wt % to about 0.2 wt % based on the total weight of the palladium and the carrier. Also disclosed is a palladium catalyst composition consisting essentially of palladium supported on α-Al2O3 wherein the palladium concentration is from about 0.001 wt % to about 0.2 wt % based on the total weight of the palladium and the α-Al2O3. Also disclosed is a hydrogenation process comprising (a) passing a mixture comprising fluoroolefin and H2 through a bed of palladium catalyst in a reaction zone wherein the palladium catalyst comprises palladium supported on a carrier; and (b) producing a hydrofluoroalkane product; characterized by: the palladium catalyst in the front of the bed having lower palladium concentration than the palladium catalyst in the back of the bed.

CROSS REFERENCE TO RELATED APPLICATIONS

The present application is a continuation of U.S. application Ser. No. 16/849,059, filed on Apr. 15, 2020, which is a continuation of U.S. application Ser. No. 16/291,548, filed on Mar. 4, 2019, now U.S. Pat. No. 10,633,311, which is a continuation of U.S. application Ser. No. 15/415,960, filed on Jan. 26, 2017, now U.S. Pat. No. 10,221,113, which is a divisional application of U.S. Ser. No. 14/115,661, filed on Nov. 5, 2013, now U.S. Pat. No. 9,598,336, which is a '371 of international application having Serial Number PCT/US2012/03822, filed on May 16, 2012, which claims benefit of U.S. Ser. No. 61/486,472, filed on May 16, 2011, the contents of all of which are incorporated by reference.

BACKGROUND Field of the Disclosure

This disclosure relates in general to the hydrogenation reactions of fluoroolefins with H₂ in the presence of a palladium catalyst supported on a carrier, compositions of palladium supported on α-Al₂O₃ and their use in the fluoroolefin hydrogenation processes.

Description of Related Art

Hydrofluoroalkanes can be employed in a wide range of applications, including their use as refrigerants, solvents, foam expansion agents, cleaning agents, aerosol propellants, dielectrics, fire extinguishants and power cycle working fluids. For example, HFC-236ea (CF₃CHFCHF₂) can be used as a heat transfer medium, foam expansion agent, fire extinguishant, et al. Similarly, HFC-245eb (CF₃CHFCH₂F) can be used as a heat transfer medium, foam expansion agent, et al. HFC-236ea and HFC-245eb are also intermediates in the production of HFO-1234yf (CF₃CF═CH₂) which is a refrigerant with zero ozone depletion potential and low global warming potential.

BRIEF SUMMARY OF THE DISCLOSURE

The present disclosure provides a hydrogenation process. The process comprises reacting a fluoroolefin with H₂ in a reaction zone in the presence of a palladium catalyst to produce a hydrofluoroalkane product, wherein said palladium catalyst comprises palladium supported on a carrier wherein the palladium concentration is from about 0.001 wt % to about 0.2 wt % based on the total weight of the palladium and the carrier.

The present disclosure also provides a palladium catalyst composition consisting essentially of palladium supported on α-Al₂O₃ wherein the palladium concentration is from about 0.001 wt % to about 0.2 wt % based on the total weight of the palladium and the α-Al₂O₃.

The present disclosure also provides a hydrogenation process comprising reacting a fluoroolefin with H₂ in a reaction zone in the presence of a palladium catalyst to produce a hydrofluoroalkane product, characterized by: said palladium catalyst consisting essentially of palladium supported on α-Al₂O₃ wherein the palladium concentration is from about 0.001 wt % to about 0.2 wt % based on the total weight of the palladium and the α-Al₂O₃.

The present disclosure also provides a hydrogenation process comprising (a) passing a mixture comprising fluoroolefin and H₂ through a bed of palladium catalyst in a reaction zone wherein the palladium catalyst comprises palladium supported on a carrier; and (b) producing a hydrofluoroalkane product; characterized by: the palladium catalyst in the front of the bed having lower palladium concentration than the palladium catalyst in the back of the bed.

DETAILED DESCRIPTION

The hydrogenation reactions of fluoroolefins can be highly exothermic, which can lead to poor temperature control, high levels of undesired byproducts, and safety concerns, et al. Some approaches have been explored to control the heat. For example, Van Der Puy et al. used multiple vapor phase reaction stages as disclosed in U.S. Pat. No. 7,560,602. Also disclosed in U.S. Pat. No. 7,560,602 is an approach of using 1 wt % Pd/C catalysts diluted with inert protruded packing. However, the multiple-reaction-stage design is costly requiring multiple reactors and heat exchangers. The approach of using high Pd loaded (e.g., 1 wt %) catalysts diluted with inert packing could cause highly localized hot spots on the catalyst surface and sintering of highly valuable Pd. Thus, there is a need for cost-effective hydrogenation processes with good heat control.

The foregoing general description and the following detailed description are exemplary and explanatory only and are not restrictive of the invention, as defined in the appended claims. Other features and benefits of any one or more of the embodiments will be apparent from the following detailed description, and from the claims.

As used herein, the terms “comprises,” “comprising,” “includes,” “including,” “has,” “having” or any other variation thereof, are intended to cover a non-exclusive inclusion. For example, a process, method, article, or apparatus that comprises a list of elements is not necessarily limited to only those elements but may include other elements not expressly listed or inherent to such process, method, article, or apparatus. Further, unless expressly stated to the contrary, “or” refers to an inclusive or and not to an exclusive or. For example, a condition A or B is satisfied by any one of the following: A is true (or present) and B is false (or not present), A is false (or not present) and B is true (or present), and both A and B are true (or present).

Also, use of “a” or “an” are employed to describe elements and components described herein. This is done merely for convenience and to give a general sense of the scope of the invention. This description should be read to include one or at least one and the singular also includes the plural unless it is obvious that it is meant otherwise.

Unless otherwise defined, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. In case of conflict, the present specification, including definitions, will control. Although methods and materials similar or equivalent to those described herein can be used in the practice or testing of embodiments of the present invention, suitable methods and materials are described below. In addition, the materials, methods, and examples are illustrative only and not intended to be limiting.

When an amount, concentration, or other value or parameter is given as either a range, preferred range or a list of upper preferable values and/or lower preferable values, this is to be understood as specifically disclosing all ranges formed from any pair of any upper range limit or preferred value and any lower range limit or preferred value, regardless of whether ranges are separately disclosed. Where a range of numerical values is recited herein, unless otherwise stated, the range is intended to include the endpoints thereof, and all integers and fractions within the range.

The term “an elevated temperature”, as used herein, means a temperature higher than the room temperature.

The term “hydrogenation”, as used herein, means a process during which a pair of hydrogen atoms is added to a double bond in an olefin.

The term “fluoroolefin”, as used herein, means a molecule containing carbon, fluorine, optionally hydrogen, and at least one carbon-carbon double bond. Of note are fluoroolefins of the formula C_(n)H_(m)F_(2n-m) wherein n is an integer from 2 to 8 and m is an integer from 0 to 2n−1. In some embodiments of this invention, n is an integer from 2 to 7. In some embodiments of this invention, the fluoroolefins are terminal fluoroolefins (i.e., the carbon-carbon double bond is at the terminal position) having 3 to 8 carbons. In some embodiments of this invention, the fluoroolefins are terminal fluoroolefins having 3 to 7 carbons. Exemplary fluoroolefins in this disclosure include CF₃CF═CF₂ (HFP), CF₃CF═CHF (HFO-1225ye), CF₃CH═CF₂, CF₃CF═CH₂, CF₃CH═CHF, CF₃CF═CFCF₃, CF₃CH═CHCF₃, CF₃CH═CFCF₃, CF₃CF₂CF═CFCF₃, CF₃CF₂CH═CHCF₃, (CF₃)₂CFCF═CF₂, CF₃CF═CHC₂F₅, CF₃CH═CFC₂F₅, C₄F₉CH═CH₂, CF₃CF₂CF₂CF₂CF═CFCF₃, CF₃CF₂CF₂CF═CFCF₂CF₃, C₂F₅CH═CFCF₂C₂F₅, C₂F₅CF═CHCF₂C₂F₅, and mixtures thereof.

The term “hydrofluoroalkane”, as used herein, means a saturated molecule containing hydrogen, carbon, and fluorine.

Disclosed is a hydrogenation process comprising reacting a fluoroolefin with H₂ in a reaction zone in the presence of a palladium catalyst to produce a hydrofluoroalkane product, wherein said palladium catalyst comprises palladium supported on a carrier wherein the palladium concentration is from about 0.001 wt % to about 0.2 wt % based on the total weight of the palladium and the carrier. In some embodiments of this invention, the palladium catalyst consists essentially of palladium supported on a carrier wherein the palladium concentration is from about 0.001 wt % to about 0.2 wt % based on the total weight of the palladium and the carrier.

In some embodiments of this invention, the palladium concentration of the palladium catalyst is from about 0.001 wt % to about 0.08 wt % based on the total weight of the palladium and the carrier. In some embodiments of this invention, the palladium concentration of the palladium catalyst is from about 0.001 wt % to about 0.04 wt % based on the total weight of the palladium and the carrier. In some embodiments of this invention, the palladium concentration of the palladium catalyst is from about 0.015 wt % to about 0.025 wt % based on the total weight of the palladium and the carrier.

Also disclosed is a palladium catalyst composition consisting essentially of palladium supported on α-Al₂O₃ wherein the palladium concentration is from about 0.001 wt % to about 0.2 wt % based on the total weight of the palladium and the α-Al₂O₃. Also disclosed is the use of such Pd/α-Al₂O₃ composition as a catalyst in a hydrogenation process. Accordingly, this disclosure also provides a hydrogenation process comprising reacting a fluoroolefin with H₂ in a reaction zone in the presence of a palladium catalyst to produce a hydrofluoroalkane product, characterized by: said palladium catalyst consisting essentially of palladium supported on α-Al₂O₃ wherein the palladium concentration is from about 0.001 wt % to about 0.2 wt % based on the total weight of the palladium and the α-Al₂O₃.

In some embodiments of this invention, the palladium concentration of the Pd/α-Al₂O₃ composition is from about 0.001 wt % to about 0.08 wt % based on the total weight of the palladium and the α-Al₂O₃. In some embodiments of this invention, the palladium concentration of the Pd/α-Al₂O₃ composition is from about 0.001 wt % to about 0.04 wt % based on the total weight of the palladium and the α-Al₂O₃. In some embodiments of this invention, the palladium concentration of the Pd/α-Al₂O₃ composition is from about 0.015 wt % to about 0.025 wt % based on the total weight of the palladium and the α-Al₂O₃.

In some embodiments of this invention, the fluoroolefin starting material is C_(n)H_(m)F_(2n-m) and the hydrofluoroalkane product is C_(n)H_(m+2)F_(2n-m), wherein n is an integer from 2 to 8 and m is an integer from 0 to 2n−1. In some embodiments of this invention, the fluoroolefin starting material is CF₃CF═CF₂ and the hydrofluoroalkane product is CF₃CHFCHF₂. In some embodiments of this invention, the fluoroolefin starting material is CF₃CF═CHF and the hydrofluoroalkane product is CF₃CHFCH₂F. In some embodiments of this invention, the fluoroolefin starting material is a mixture of two or more fluoroolefins. For example, the fluoroolefin starting material can be a mixture of CF₃CF═CF₂ and CF₃CF═CHF, and the corresponding hydrofluoroalkane product is a mixture of CF₃CHFCHF₂ and CF₃CHFCH₂F. For another example, the fluoroolefin starting material can be a mixture of CF₃CF═CF₂ and CF₃CF═CFCF₃, and the corresponding hydrofluoroalkane product is a mixture of CF₃CHFCHF₂ and CF₃CHFCHFCF₃. For yet another example, the fluoroolefin starting material can be a mixture of CF₃CF═CF₂ and CF₃CF═CFC₂F₅, and the corresponding hydrofluoroalkane product is a mixture of CF₃CHFCHF₂ and CF₃CHFCHFC₂F₅. For yet another example, the fluoroolefin starting material can be a mixture of CF₃CF═CFC₂F₅ and C₂F₅CF═CFCF₂C₂F₅, and the corresponding hydrofluoroalkane product is a mixture of CF₃CHFCHFC₂F₅ and C₂F₅CHFCHFCF₂C₂F₅. For yet another example, the fluoroolefin starting material can be a mixture of CF₃CF═CHC₂F₅ and CF₃CH═CFC₂F₅, and the corresponding hydrofluoroalkane product is a mixture of CF₃CHFCH₂C₂F₅ and CF₃CH₂CHFC₂F₅. For yet another example, the fluoroolefin starting material can be a mixture of CF₃CF═CHF, CF₃CF═CHC₂F₅ and CF₃CH═CFC₂F₅, and the corresponding hydrofluoroalkane product is a mixture of CF₃CHFCH₂F, CF₃CHFCH₂C₂F₅ and CF₃CH₂CHFC₂F₅. For yet another example, the fluoroolefin starting material can be a mixture of CF₃CF═CHF and CF₃CH═CFCF₃, and the corresponding hydrofluoroalkane product is a mixture of CF₃CHFCH₂F and CF₃CH₂CHFCF₃.

Some fluoroolefins in this disclosure, e.g., HFO-1225ye, exist as different configurational isomers or stereoisomers. When the specific isomer is not designated, the present disclosure is intended to include all configurational isomers, stereoisomers, or any combination thereof. For instance, HFO-1225ye is meant to represent the E-isomer, Z-isomer, or any combination or mixture of both isomers in any ratio.

The hydrogenation reactions between fluoroolefin and H₂ are carried out in the presence of a palladium catalyst. The palladium catalyst in this disclosure is a finely divided zero valent palladium metal supported on a carrier. In some embodiments of this invention, the carrier is selected from the group consisting of Al₂O₃, fluorinated Al₂O₃, AlF₃, carbon, Cr₂O₃, SiO₂, TiO₂, ZrO₂ and ZnO.

In some embodiments of this invention, the carrier is carbon. Carbon used in the embodiments of this invention may come from any of the following sources: wood, peat, coal, coconut shells, bones, lignite, petroleum-based residues and sugar. Commercially available carbons which may be used include those sold under the following trademarks: Barneby & Sutcliffe™, Darco™, Nucharm, Columbia JXN™, Columbia LCK™, Calgon™ PCB, Calgon™ BPL, Westvaco™, Norit™, Takeda and Barnaby Cheny NB™.

The carbon also includes three dimensional matrix porous carbonaceous materials. Examples are those described in U.S. Pat. No. 4,978,649. In some embodiments of the invention, carbon includes three dimensional matrix carbonaceous materials which are obtained by introducing gaseous or vaporous carbon-containing compounds (e.g., hydrocarbons) into a mass of granules of a carbonaceous material (e.g., carbon black); decomposing the carbon-containing compounds to deposit carbon on the surface of the granules; and treating the resulting material with an activator gas comprising steam to provide a porous carbonaceous material. A carbon-carbon composite material is thus formed.

Carbon includes unwashed and acid-washed carbons. In some embodiments of this invention, suitable carbon carrier may be prepared by treating the carbon with acids such as HNO₃, HCl, HF, H₂SO₄, HClO₄, CH₃COOH, and combinations thereof. In some embodiments of this invention, acid is HCl or HNO₃. Acid treatment is typically sufficient to provide carbon that contains less than 1000 ppm of ash. Some suitable acid treatments of carbon are described in U.S. Pat. No. 5,136,113. In some embodiments of this invention, a carbon carrier is soaked overnight with gentle stirring in a 1 molar solution of the acid prepared in deionized water. The carbon carrier is then separated and washed at least 10 times with deionized water or until the pH of the washings is about 3. (In some embodiments of this invention, the carbon carrier is then soaked again with gentle stirring in a 1 molar solution of the acid prepared in deionized water for 12 to 24 hours.) The carbon carrier is then finally washed with deionized water until the washings are substantially free of the anion of the acid (e.g., Cl⁻ or NO₃ ⁻), when tested by standard procedures. The carbon carrier is then separated and dried at 120° C. The washed carbon is then soaked in 1 molar HF prepared in deionized water for 48 hours at room temperature with occasional stirring (e.g., in a plastic beaker). The carbon carrier is separated and washed repeatedly with deionized water at 50° C. until the pH of the washings is greater than 4. The carbon carrier is then dried at 150° C. for 60 hours in air followed by calcination at 300° C. for 3 hours in air prior to its use as a carrier.

In some embodiments of this invention, carbon is an activated carbon. In some embodiments of this invention, carbon is an acid washed activated carbon. The carbon can be in the form of powder, granules, or pellets, et al.

In some embodiments of this invention, the carrier is Al₂O₃. Al₂O₃, also known as alumina, exists in several different phases, e.g., α-, γ-, δ-, η-, θ-, and χ-aluminas. In α-Al₂O₃ (corundum), the oxide ions form a hexagonal close-packed structure and the aluminum ions are distributed symmetrically among the octahedral interstices (see F. A. Cotton and G. Wilkinson, Advanced Inorganic Chemistry, Fifth Edition, John Wiley & Sons, 1988, page 211). γ-Al₂O₃ has a “defect” spinel structure (the structure of spinel with a deficit of cations). Id. In some embodiments of this invention, the carrier is α-Al₂O₃. It was surprisingly found through experiments that the hydrogenation processes using α-Al₂O₃ as the carrier for the palladium catalysts generate fewer byproducts than other similar hydrogenation processes do when other types of alumina (e.g., γ-Al₂O₃) are used as the carriers.

Alumina may be prepared by methods known in the art. For example, the Bayer process is widely used in the industry to produce alumina from bauxite. α-Al₂O₃ can be prepared by heating γ-Al₂O₃ or any hydrous oxide above 1000° C. Id. γ-Al₂O₃ can be prepared by dehydration of hydrous oxides at about 450° C. Id.

The alumina used in this disclosure can be of any suitable shape and dimensions. For example, alumina can be in the form of powder, granules, spheres, or tablets, et al. Typically, alumina used in this disclosure has surface area of from about 1 m²/g to about 500 m²/g. In some embodiments of this invention, the alumina has surface area of from about 1 m²/g to about 200 m²/g. In some embodiments of this invention, the alumina has surface area of from about 1 m²/g to about 50 m²/g. In some embodiments of this invention, the alumina has surface area of from about 1 m²/g to about 10 m²/g. In some embodiments of this invention, the alumina has surface area of from about 3 m²/g to about 7 m²/g.

Palladium can be deposited on the carrier using techniques known in the art. For example, the palladium catalysts may be prepared by impregnation methods as generally described by Satterfield on pages 93-112 in Heterogeneous Catalysis in Industrial Practice, 2^(nd) edition (McGraw-Hill, New York, 1991). Typically, in an impregnation process, a palladium salt is dissolved in a solvent to form a palladium salt solution. Examples of suitable palladium salts for this disclosure include palladium nitrate, palladium chloride, palladium acetate and palladium ammine complexes. Examples of suitable solvents include water and alcohols (e.g., methanol, ethanol, propanol, isopropanol). A carrier is then impregnated with the palladium salt solution. In some embodiments of this invention, a carrier is dipped into an excess amount of the palladium salt solution. In some embodiments of this invention, the incipient wetness technique is used for the impregnation. In an incipient wetness process, a batch of carrier is tumbled and sprayed with an appropriate amount of the palladium salt solution (the amount of the solution is calculated to be just sufficient or slightly less to fill the pores of the carrier). The concentration of the palladium salt solution may be calculated or adjusted so that the finished catalyst has the desired concentration of palladium loaded on the carrier. The incipient wetness technique is also described by Bailey in U.S. Patent Application Publication No. 2006/0217579.

The impregnated carrier is then dried, typically at an elevated temperature. Optionally, the dried impregnated carrier is calcined. The calcination is typically carried out at a temperature of from about 100° C. to about 600° C. In some embodiments of this invention, the calcination is carried out in the presence of an inert gas (e.g., nitrogen, argon) and/or oxygen. The resulting catalyst is then typically treated with a reducing agent prior to use. In some embodiments of this invention, the resulting catalyst is reduced in a flow of hydrogen at an elevated temperature. The hydrogen flow may be diluted with inert gas such as nitrogen, helium, or argon. The reduction temperature is typically from about 100° C. to about 500° C. In some embodiments of this invention, the reduction may be carried out in a liquid phase by hydrazine or formic acid as described by Boitiaux et al. in U.S. Pat. No. 4,533,779.

The hydrogenation process can be carried out in the liquid phase or vapor phase using well-known chemical engineering practice, which includes continuous, semi-continuous or batch operations.

In some embodiments of this invention, the hydrogenation process is carried out in the liquid phase. The liquid phase hydrogenation reaction temperature is typically from about 0° C. to about 200° C. In some embodiments of this invention, the liquid phase hydrogenation reaction temperature is from about 25° C. to about 100° C. The pressure of the liquid phase hydrogenation may vary widely from less than 1 atmosphere to 30 atmospheres or more.

Optionally, the liquid phase hydrogenation process is carried out in the presence of a solvent. The solvent can be polar or non-polar. Suitable polar solvents include water, alcohols, glycol, acetic acid, dimethylformamide (DMF), N-methylpyrrolidone (NMP), triethylamine, and mixtures thereof. In some embodiments of this invention, the polar solvent is methanol, ethanol, or mixtures thereof. Suitable non-polar solvents include inert low dielectric alkanes (e.g., nonane and cyclohexane) and inert low dielectric aromatics (e.g., toluene, benzene and ortho xylene). In some embodiments of this invention, the solvent can also be the expected hydrofluoroalkane product.

In some embodiments of this invention, the hydrogenation process is carried out in the vapor phase. The vapor phase hydrogenation reaction temperature is typically from about room temperature to about 300° C. In some embodiments of this invention, the vapor phase hydrogenation reaction temperature is from about 50° C. to about 200° C.

The vapor phase hydrogenation process can be conducted at superatmospheric, atmospheric, or subatmospheric pressures. In some embodiments of this invention, the vapor phase hydrogenation reaction pressure is from about 10 psig to about 500 psig. In some embodiments of this invention, the vapor phase hydrogenation reaction pressure is from about 50 psig to about 200 psig.

The vapor phase hydrogenation process of this disclosure may be conducted by methods known in the art. In some embodiments of this invention, the fluoroolefin and H₂ starting materials, optionally with a diluent, are co-fed to a reactor containing the palladium catalyst. In some embodiments of this invention, the fluoroolefin and H₂ starting materials, optionally with a diluent, are passed through the palladium catalyst bed in a reactor.

In some embodiments of this invention, the vapor phase hydrogenation process is conducted without a diluent.

In some embodiments of this invention, the vapor phase hydrogenation process is conducted in the presence of a diluent. In some embodiments of this invention, the diluent is co-fed to the reaction zone with the fluoroolefin and H₂ starting materials. In some embodiments of this invention, the molar ratio of the diluent to fluoroolefin starting material co-fed to the reaction zone is from about 100:1 to about 1:1. In some embodiments of this invention, the molar ratio of the diluent to fluoroolefin starting material co-fed to the reaction zone is from about 10:1 to about 1:1. In some embodiments of this invention, the molar ratio of the diluent to fluoroolefin starting material co-fed to the reaction zone is from about 5:1 to about 1:1. The diluent can be an inert gas which does not react under the hydrogenation conditions of this disclosure. In some embodiments of this invention, the diluent is He, Ar, or N₂. The diluent can also be the expected hydrofluoroalkane product. For example, when fluoroolefin starting material is HFP, HFC-236ea can be used as the diluent to control the reaction temperature. In some embodiments of this invention, the HFC-236ea diluent is co-fed with HFP and H₂ to the reaction zone. For another example, when fluoroolefin starting material is HFO-1225ye, HFC-245eb can be used as the diluent to control the reaction temperature. In some embodiments of this invention, the HFC-245eb diluent is co-fed with HFO-1225ye and H₂ to the reaction zone.

In some embodiments of this invention, the diluent is selected from the group consisting of saturated hydrocarbons and saturated hydrofluorocarbons. Suitable saturated hydrocarbons include C1 to C8 alkanes such as methane, ethane, propane et al. Suitable saturated hydrofluorocarbons include C1 to C8 saturated hydrofluorocarbons such as CHF₃, CH₂F₂, CHF₂CF₃, CHF₂CHF₂, CH₂FCF₃, CF₃CF₃, CF₃CF₂CF₃, CF₃CHFCH₂F, CF₃CH₂CHF₂, CF₃CHFCH₃, CF₃CH₂CH₂F, CF₃CHFCHF₂, CF₃CH₂CF₃, CF₃CF₂CH₂F, CF₃CH₂CH₂CF₃, CF₃CHFCHFC₂F₅, C₆F₁₄, and C₂F₅CHFCHFC₃F₇.

The molar ratio of H₂ to fluoroolefin fed to the reaction zone in the vapor phase hydrogenation process can be largely varied. Typically, the molar ratio of H₂ to fluoroolefin fed to the reaction zone in the vapor phase hydrogenation process is from about 0.1:1 to about 100:1. In some embodiments of this invention, the molar ratio is from about 0.5:1 to about 5:1. In some embodiments of this invention, the molar ratio is from about 0.9:1 to about 3:1.

The effluent from the vapor phase hydrogenation reaction zone is typically a product mixture comprising unreacted starting materials, diluent (if used in the process), the desired hydrofluoroalkane product and some byproducts. The desired hydrofluoroalkane product may be recovered from the product mixture by conventional methods. In some embodiments of this invention, the desired hydrofluoroalkane product may be purified or recovered by distillation. In some embodiments of this invention, the unreacted starting materials, and optionally diluent (if used in the process), are recovered and recycled back to the reaction zone.

Also disclosed is a hydrogenation process comprising (a) passing a gaseous or liquid mixture comprising fluoroolefin and H₂ through a bed of palladium catalyst in a reaction zone wherein the palladium catalyst comprises palladium supported on a carrier; and (b) producing a hydrofluoroalkane product; characterized by: the palladium catalyst in the front of the bed having lower palladium concentration than the palladium catalyst in the back of the bed. The front of the bed is the flow entrance to the catalyst bed, and the back of the bed is the flow exit from the catalyst bed. In some embodiments of this invention, the palladium concentration of the catalyst in the front of the bed is from about 0.001 wt % to about 0.2 wt % based on the total weight of the palladium and the carrier, and the palladium concentration of the catalyst in the back of the bed is from about 0.1 wt % to about 1 wt % based on the total weight of the palladium and the carrier. In some embodiments of this invention, the palladium concentration of the catalyst in the front of the bed is from about 0.001 wt % to about 0.08 wt % based on the total weight of the palladium and the carrier, and the palladium concentration of the catalyst in the back of the bed is from about 0.2 wt % to about 0.8 wt % based on the total weight of the palladium and the carrier. In some embodiments of this invention, the palladium concentration of the catalyst in the front of the bed is from about 0.001 wt % to about 0.04 wt % based on the total weight of the palladium and the carrier, and the palladium concentration of the catalyst in the back of the bed is from about 0.3 wt % to about 0.6 wt % based on the total weight of the palladium and the carrier. In some embodiments of this invention, the palladium concentration of the catalyst in the front of the bed is from about 0.015 wt % to about 0.025 wt % based on the total weight of the palladium and the carrier, and the palladium concentration of the catalyst in the back of the bed is from about 0.3 wt % to about 0.6 wt % based on the total weight of the palladium and the carrier.

In some embodiments of this invention, the catalyst bed comprises two or more sections with the same or different lengths wherein each section comprises palladium catalysts having the same palladium concentration. For example, the catalyst bed can comprise a front section and a back section, wherein the front section comprises palladium catalysts with 0.02 wt % palladium concentration and the back section comprises palladium catalysts with 0.5 wt % palladium concentration, and wherein the length of the front section is about 60% of the total bed length and the length of the back section is about 40% of the total bed length. In some embodiments of this invention, the catalyst bed comprises palladium catalysts with continuously increasing palladium concentrations from the front to the back of the catalyst bed.

The reactors, distillation columns, and their associated feed lines, effluent lines, and associated units used in applying the processes of embodiments of this invention may be constructed of materials resistant to corrosion. Typical materials of construction include Teflon™ and glass. Typical materials of construction also include stainless steels, in particular of the austenitic type, the well-known high nickel alloys, such as MoneI™ nickel-copper alloys, Hastelloy™ nickel-based alloys and, Inconel™ nickel-chromium alloys, and copper-clad steel.

EXAMPLES

The concepts described herein will be further described in the following examples, which do not limit the scope of the invention described in the claims.

LEGEND 245eb is CF₃CHFCH₂F 236ea is CF₃CHFCHF₂ HFP is CF₃CF═CF₂ 254eb is CH₃CHFCF₃ 1225ye is CF₃CF═CHF

General Procedure for Examples 1-5

The following general procedure is illustrative of the reactor and the thermocouple layout for the temperature measurement. The hydrogenation reaction was carried out by passing a gaseous mixture through a bed of palladium catalyst. 1225ye used herein contained 97-98% Z isomers and 2-3% E isomers. Part of the reactor effluent was sampled on-line for organic product analysis using GC-FID (Gas Chromatograph-Flame Ionization Detector).

A vertically oriented Hastelloy™ reactor (1 inch OD, 0.065 inch wall) jacketed by a recirculating hot oil system was used in all the experiments described below. The reactor was charged with 28.6 cm³ palladium catalysts in the form of ⅛ inch spheres or ⅛ inch×⅛ inch tablets. The palladium catalyst bed in the reactor rose to 3 inches in height and was packed between ⅛ inch Denstone™ α-Al₂O₃ spheres (on top) and ¼ inch Hastelloy™ protruded packing (at the bottom).

The gaseous mixture of starting materials and a diluent was preheated and passed through the reactor entering at the top and exiting at the bottom. A ⅛ inch thermocouple situated along the center of the reactor measured the temperature profile at 8 points: −0.5 inch, 0 inch, 0.5 inch, 1 inch, 1.5 inch, 2 inch, 2.5 inch, and 3 inch. The point of “−0.5 inch” was about 0.5 inch above the catalyst bed; the point of “0 inch” was at about the top of the catalyst bed; and the point of “0.5 inch” was about 0.5 inch below the top of the catalyst bed; and so on.

Example 1

Example 1 demonstrates that hydrogenation of HFP over 0.1 wt % Pd/α-Al₂O₃ has good control of heat and produces good yields of HFC-236ea with high selectivity.

A gaseous mixture of HFP, H₂, and 236ea was fed into the reactor. The HFP flow rate is shown in Table 1. The amount of H₂ or 236ea relative to HFP in the gaseous mixture is also shown in Table 1. Table 1 also shows the temperature profile in the reactor and the analytical results of the composition of the effluent from the reactor.

TABLE 1 (Part A) Feed Rate Reactor Effluent HFP Molar Feed Ratios Pressure (mol %) Run (g/h) H₂/HFP 236ea/HFP (psig) HFP 236ea 245eb 1 454 2.0 5.0 59 4.8 95.2 0.02 2 454 2.0 5.0 60 6.6 93.3 0.01 3 451 2.0 6.0 60 7.6 92.4 0.01 4 454 2.0 7.0 61 7.8 92.2 0.01 5 455 3.0 6.0 60 8.0 92.0 0.01 6 452 4.0 5.0 60 8.0 91.9 0.01 7 454 2.0 6.8 60 8.2 91.7 0.01 8 452 2.0 7.0 61 7.6 92.4 0.01 9 454 2.0 7.0 61 6.7 93.2 0.01 10 454 2.0 7.0 61 6.7 93.3 0.01 11 457 2.0 6.9 60 6.0 93.9 0.01

TABLE 1 (Part B) Hot Oil Internal Temperatures (° C.) Run (° C.) −0.5″ 0″ 0.5″ 1″ 1.5″ 2″ 2.5″ 3″ 1 74 80 79 78 78 81 118 159 166 2 65 75 73 72 71 72 96 132 143 3 65 75 74 72 71 72 86 110 119 4 65 78 76 74 72 73 83 98 106 5 65 76 74 72 71 72 85 106 116 6 65 74 72 71 70 71 88 117 130 7 65 76 75 73 72 72 81 95 102 8 74 81 80 79 78 79 91 107 114 9 84 85 85 85 85 87 101 121 130 10 94 91 92 92 93 95 110 130 138 11 104 95 97 98 99 102 121 144 152

Example 2

Example 2 demonstrates that hydrogenation of HFP over 0.04 wt % Pd/α-Al₂O₃ has good control of heat and produces good yields of HFC-236ea with high selectivity.

A gaseous mixture of HFP, H₂, and 236ea was fed into the reactor. The HFP flow rate is shown in Table 2. The amount of H₂ or 236ea relative to HFP in the gaseous mixture is also shown in Table 2. Table 2 also shows the temperature profile in the reactor and the analytical results of the composition of the effluent from the reactor.

TABLE 2 (Part A) Feed Rate Reactor HFP Molar Feed Ratios Pressure Effluent (mol %) Run (g/h) H₂/HFP 236ea/HFP (psig) HFP 236ea 245eb 1 91 2.0 10.0 125 1.4 98.5 0.03 2 138 2.0 6.6 125 1.5 98.5 0.03 3 228 2.0 3.9 125 2.2 97.7 0.04 4 226 1.2 3.0 125 4.4 95.6 0.03 5 226 1.2 5.0 100 6.5 93.5 0.01 6 227 2.0 5.0 100 5.6 94.4 0.01 7 226 3.0 5.1 100 5.3 94.7 0.01 8 226 3.0 4.9 100 4.8 95.1 0.01 9 227 3.0 5.0 100 4.3 95.7 0.01 10 226 2.0 5.0 100 7.5 92.5 0.01

TABLE 2 (Part B) Hot Oil Internal Temperatures (° C.) Run (° C.) −0.5″ 0″ 0.5″ 1″ 1.5″ 2″ 2.5″ 3″ 1 84 86 97 116 130 134 134 131 127 2 85 87 103 132 151 155 154 149 143 3 84 88 110 154 180 185 182 174 166 4 84 89 121 172 195 196 189 179 168 5 84 86 95 113 129 138 143 145 143 6 84 86 95 115 132 142 147 149 147 7 85 86 95 115 132 143 148 150 148 8 94 95 105 127 144 155 159 161 159 9 104 104 116 140 159 168 172 172 169 10 114 114 124 144 158 165 167 167 165

Example 3

Example 3 demonstrates that hydrogenation of HFP over 0.02 wt % Pd/α-Al₂O₃ has good control of heat and produces good yields of HFC-236ea with high selectivity.

A gaseous mixture of HFP, H₂, and 236ea was fed into the reactor. The HFP flow rate is shown in Table 3. The amount of H₂ or 236ea relative to HFP in the gaseous mixture is also shown in Table 3. Table 3 also shows the temperature profile in the reactor and the analytical results of the composition of the effluent from the reactor.

TABLE 3 (Part A) Feed Rate Reactor HFP Molar Feed Ratios Pressure Effluent (mol %) Run (g/h) H₂/HFP 236ea/HFP (psig) HFP 236ea 245eb 1 91 2.0 9.9 100  6.2% 93.7% 0.02% 2 137 2.0 6.7 99  8.6% 91.4% 0.02% 3 227 3.0 4.0 100 12.9% 87.0% 0.02% 4 228 3.0 3.0 102 11.9% 88.0% 0.03% 5 135 2.0 6.8 100  9.1% 90.9% 0.01% 6 226 2.0 4.0 100 13.3% 86.7% 0.01% 7 226 3.0 3.1 101 14.3% 85.6% 0.02% 8 227 3.0 3.0 125  8.6% 91.3% 0.05% 9 226 3.0 3.0 125 11.3% 88.7% 0.01% 10 227 1.2 2.9 125 13.7% 86.3% 0.01% 11 226 1.2 3.0 125  9.3% 90.7% 0.02% 12 228 1.2 3.0 125 14.9% 85.1% 0.01% 13 227 3.0 3.0 125 11.9% 88.1% 0.01% 14 226 1.2 2.0 125 10.8% 89.1% 0.02% 15 229 0.5 2.0 125 24.2% 75.7% 0.00% 16 228 1.2 2.2 125 10.9% 89.1% 0.02% 17 227 3.0 3.0 125 14.0% 85.9% 0.01%

TABLE 3 (Part B) Hot Oil Internal Temperatures (° C.) Run (° C.) −0.5″ 0″ 0.5″ 1″ 1.5″ 2″ 2.5″ 3″ 1 84 85 88 91 93 96 98 100 2 84 84 85 89 93 96 101 105 108 3 84 85 86 90 96 101 110 118 124 4 84 85 86 92 101 111 127 142 152 5 85 84 85 88 91 94 99 103 106 6 84 84 85 89 94 99 107 115 121 7 84 85 86 90 97 104 117 130 138 8 85 94 98 108 123 140 160 173 177 9 94 85 87 94 105 117 135 149 158 10 85 94 97 105 117 129 143 153 159 11 94 114 120 137 162 180 193 197 194 12 114 84 87 93 102 111 124 133 139 13 84 85 87 93 104 114 130 142 151 14 84 85 91 107 136 164 188 194 189 15 85 85 87 94 104 113 123 127 128 16 84 85 92 111 142 167 186 189 181 17 84 85 87 93 101 109 120 129 136

Example 4

Example 4 demonstrates that hydrogenation of 1225ye over 0.1 wt % Pd/α-Al₂O₃ has good control of heat and produces good yields of HFC-245eb with high selectivity.

A gaseous mixture of 1225ye, H₂, and 245eb was fed into the reactor. The 1225ye flow rate is shown in Table 4. The amount of H₂ or 245eb relative to 1225ye in the gaseous mixture is also shown in Table 4.

Table 4 also shows the temperature profile in the reactor and the analytical results of the composition of the effluent from the reactor.

TABLE 4 (Part A) Feed Rate Reactor 1225ye Molar Feed Ratios Pressure Effluent (mol %) Run (g/h) H₂/1225ye 245eb (psig) 1225ye 254eb 245eb 1 91 2.0 9.9 75 1.9 0.17 97.9 2 135 2.0 6.6 75 2.5 0.16 97.4 3 226 2.0 4.0 75 2.7 0.18 97.0 4 339 2.0 2.7 75 3.9 0.22 95.8 5 226 1.5 5.9 75 4.4 0.09 95.4 6 226 2.0 4.0 76 3.0 0.12 96.8 7 227 2.0 4.0 60 3.7 0.10 96.2 8 227 2.0 4.0 60 3.6 0.09 96.3 9 227 4.0 2.1 60 2.4 0.16 97.4 10 227 3.0 3.0 60 2.7 0.12 97.2 11 227 1.5 6.0 60 5.0 0.09 94.9 12 271 1.2 4.9 60 6.5 0.09 93.4 13 343 1.2 3.7 60 7.8 0.10 92.1 14 452 1.2 2.6 60 8.4 0.12 91.5 15 226 2.0 4.0 60 4.0 0.08 95.9 16 92 2.0 9.8 60 2.8 0.06 97.1 17 228 2.0 4.0 60 4.3 0.10 95.6 18 227 0.5 4.0 60 11.2 0.09 88.7 19 225 2.0 4.0 60 4.4 0.09 95.5

TABLE 4 (Part B) Hot Oil Internal Temperatures (° C.) Run (° C.) −0.5″ 0″ 0.5″ 1″ 1.5″ 2″ 2.5″ 3″ 1 85 91 108 121 126 127 125 122 2 85 86 94 118 138 145 146 143 138 3 85 87 100 139 172 182 181 175 167 4 84 87 102 156 202 215 215 208 197 5 84 82 86 102 122 134 140 144 143 6 85 87 97 132 166 178 180 175 167 7 85 87 97 130 163 176 178 174 166 8 85 77 86 118 152 167 169 166 158 9 75 77 95 155 195 196 184 167 152 10 75 77 90 135 175 185 181 172 160 11 75 77 80 93 111 123 130 134 132 12 75 77 81 97 119 133 140 144 142 13 75 77 82 102 132 150 159 163 160 14 75 77 86 119 166 189 198 199 193 15 75 77 84 112 147 164 168 166 159 16 75 76 79 88 99 106 109 111 109 17 75 77 83 106 140 159 166 166 160 18 75 78 83 99 117 124 124 122 117 19 75 77 84 109 144 162 167 166 159

Example 5

Example 5 demonstrates that hydrogenation of 1225ye over 0.02 wt % Pd/α-Al₂O₃ has good control of heat and produces good yields of HFC-245eb with high selectivity.

A gaseous mixture of 1225ye, H₂, and 245eb was fed into the reactor. The 1225ye flow rate is shown in Table 5. The amount of H₂ or 245eb relative to 1225ye in the gaseous mixture is also shown in Table 5. Table 5 also shows the temperature profile in the reactor and the analytical results of the composition of the effluent from the reactor.

TABLE 5 (Part A) Feed Rate Molar Feed Ratios Reactor 1225ye 245eb/ Pressure Effluent (mol %) Run (g/h) H₂/1225ye 1225ye (psig) 1225ye 254eb 245eb 1 92 1.9 9.8 75  5.0% 0.10% 94.9% 2 138 2.0 6.6 75  6.9% 0.08% 93.0% 3 228 2.0 3.9 75 10.4% 0.09% 89.5% 4 227 3.0 2.9 74 10.7% 0.12% 89.1% 5 228 3.0 2.9 75 10.7% 0.11% 89.2% 6 226 3.0 3.0 75  9.9% 0.09% 89.9% 7 228 3.0 3.0 75  9.7% 0.09% 90.2% 8 227 3.0 3.0 75  9.4% 0.08% 90.5% 9 226 3.0 3.0 75 11.8% 0.06% 88.2% 10 228 3.0 3.0 77  9.9% 0.07% 90.0% 11 226 4.0 2.0 75  9.2% 0.10% 90.6% 12 114 2.5 7.6 75  4.7% 0.11% 95.2% 13 222 1.3 2.9 75 11.2% 0.02% 88.7% 14 114 1.2 5.6 75  9.1% 0.03% 90.8% 15 225 1.2 3.0 75 12.7% 0.03% 87.3% 16 226 2.0 3.0 75 10.8% 0.04% 89.1% 17 226 4.0 3.0 75  9.9% 0.04% 90.0% 18 227 5.9 3.0 75  9.9% 0.05% 90.0% 19 225 3.0 3.0 75 12.5% 0.04% 87.4%

TABLE 5 (Part B) Hot Oil Internal Temperatures (° C.) Run (° C.) −0.5″ 0″ 0.5″ 1″ 1.5″ 2″ 2.5″ 3″ 1 85 85 87 91 97 100 104 103 103 2 84 85 87 93 101 106 112 111 110 3 84 85 88 97 111 119 128 127 125 4 84 85 90 104 124 135 142 139 140 5 94 95 100 117 137 147 151 148 151 6 104 104 110 128 148 157 160 157 160 7 114 114 120 142 163 171 172 168 173 8 124 123 131 154 176 183 183 179 185 9 85 85 90 105 123 131 137 135 136 10 104 104 110 130 152 160 164 161 164 11 104 105 114 146 176 181 175 168 180 12 104 107 127 161 170 162 144 137 154 13 104 103 105 111 118 122 127 127 125 14 104 104 109 118 128 131 132 130 132 15 104 104 109 124 141 147 151 149 150 16 104 104 110 129 151 159 164 161 164 17 104 104 109 127 149 158 164 161 163 18 104 104 109 125 147 157 162 159 162 19 84 85 88 99 116 125 136 135 132

General Procedure for Examples 6-7

The following general procedure is illustrative of the reactor and the thermocouple layout for the temperature measurement. The hydrogenation reaction was carried out by passing a gaseous mixture through a bed of palladium catalyst. Part of the reactor effluent was sampled on-line for organic product analysis using GC-FID (Gas Chromatograph-Flame Ionization Detector).

An Inconel™ reactor (⅝ inch OD, 0.034 inch wall) jacketed by an aluminum sleeve was used in all the experiments described below. The sleeve was heated by a 5 inch long heater band furnace. The reactor was charged with 5 cm³ palladium catalysts in the form of ⅛ inch spheres or ⅛ inch×⅛ inch tablets.

The gaseous mixture of HFP, H₂, and N₂ was pre-heated to 50° C. and passed through the reactor in the direction of from the top of the catalyst bed to the bottom. The furnace temperature was controlled by a thermocouple inside the aluminum sleeve. A 1/16 inch thermocouple situated along the center of the reactor measured the temperature profile at about the top of the catalyst bed (0″ point) and about 1 inch below the top (1″ point).

Example 6

Example 6 demonstrates that hydrogenation of HFP over 0.3 wt % Pd/γ-Al₂O₃ generates considerable amount of 245eb byproduct.

A gaseous mixture of HFP, H₂, and N₂ was fed into the reactor. The HFP flow rate is shown in Table 6. The amount of H₂ and N₂ relative to HFP in the gaseous mixture is also shown in Table 6. Table 6 also shows the temperature profile in the reactor and the analytical results of the composition of the effluent from the reactor.

TABLE 6 Feed Internal Rate Temperatures Reactor Effluent HFP Molar Feed Ratios Furnace (° C.) (mol %) Run (sccm) H₂/HFP N₂/HFP (° C.) 0″ 1″ HFP 236ea 245eb 1 10 1 10 49 80 52 11.9 85.7 2.0 2 10 5 10 50 75 51 0.1 99.0 0.9 3 10 1 30 51 84 59 13.1 83.4 2.8 4 5 1 60 51 84 59 10.9 85.5 2.9 5 10 1 30 70 101 76 13.7 82.5 3.0 6 4.9 2 61 69 86 74 1.9 95.9 1.9 7 4.8 1 61 70 87 75 9.5 87.4 2.5

Example 7

Example 7 demonstrates that hydrogenation of HFP over 0.3 wt % Pd/α-Al₂O₃ does not generate 245eb byproduct.

A gaseous mixture of HFP, H₂, and N₂ was fed into the reactor. The HFP flow rate is shown in Table 7. The amount of H₂ and N₂ relative to HFP in the gaseous mixture is also shown in Table 7. Table 7 also shows the temperature profile in the reactor and the analytical results of the composition of the effluent from the reactor.

TABLE 7 Feed Internal Rate Temperatures Reactor Effluent HFP Molar Feed Ratios Furnace (° C.) (mol %) Run (sccm) H₂/HFP N₂/HFP (° C.) 0″ 1″ HFP 236ea 245eb 1 10 1 30 49 56 55 49.27 50.47 0.00 2 10 5 30 48 62 55 8.67 91.13 0.00 3 10 2.5 30 51 64 59 19.20 80.54 0.00 4 20 2.5 15 47 77 62 14.91 84.83 0.00

Note that not all of the activities described above in the general description or the examples are required, that a portion of a specific activity may not be required, and that one or more further activities may be performed in addition to those described. Still further, the order in which activities are listed are not necessarily the order in which they are performed.

In the foregoing specification, the concepts have been described with reference to specific embodiments. However, one of ordinary skill in the art appreciates that various modifications and changes can be made without departing from the scope of the invention as set forth in the claims below. accordingly, the specification is to be regarded in an illustrative rather than a restrictive sense, and all such modifications are intended to be included within the scope of invention.

Benefits, other advantages, and solutions to problems have been described above with regard to specific embodiments. However, the benefits, advantages, solutions to problems, and any feature(s) that may cause any benefit, advantage, or solution to occur or become more pronounced are not to be construed as a critical, required, or essential feature of any or all the claims.

It is to be appreciated that certain features are, for clarity, described herein in the context of separate embodiments, may also be provided in combination in a single embodiment. Conversely, various features that are, for brevity, described in the context of a single embodiment, may also be provided separately or in any subcombination. 

What is claimed is:
 1. A composition comprising a bed of a palladium catalyst supported on a carrier comprising α-Al₂O₃, the bed having a front and a back, wherein the palladium catalyst in the front of the bed has a first palladium concentration lower than a second palladium concentration of the palladium catalyst in the back of the bed.
 2. The composition according to claim 1, wherein the first palladium concentration is from about 0.001 wt % to about 0.2 wt % based on the total weight of the palladium and the carrier in the front of the bed, and the second palladium concentration is from about 0.1 wt % to about 1 wt % based on the total weight of the palladium and the carrier in the back of the bed.
 3. The composition according to claim 1, wherein the first palladium concentration is from about 0.001 wt % to about 0.08 wt % based on the total weight of the palladium and the carrier in the front of the bed, and the second palladium concentration is from about 0.2 wt % to about 0.8 wt % based on the total weight of the palladium and the carrier in the back of the bed.
 4. The composition according to claim 1, wherein the first palladium concentration is from about 0.015 wt % to about 0.025 wt % based on the total weight of the palladium and the carrier in the front of the bed, and the second palladium concentration is from about 0.3 wt % to about 0.6 wt % based on the total weight of the palladium and the carrier in the back of the bed.
 5. The composition according to claim 1, wherein the bed comprises a front section at the front of the bed and a back section at the back of the bed.
 6. The composition according to claim 5, wherein the front section has the first palladium concentration and the back section has the second palladium concentration.
 7. The composition according to claim 1, wherein a palladium concentration increases continuously from the first palladium concentration at the front of the bed to the second palladium concentration at the back of the bed.
 8. The composition according to claim 1 further comprising hydrogen (H₂).
 9. The composition according to claim 8 further comprising at least one fluoroolefin having the formula C_(n)H_(m)F_(2n-m), wherein n is an integer from 2 to 8 and m is an integer from 0 to 2n−1.
 10. The composition according to claim 1 further comprising at least one fluoroolefin having the formula C_(n)H_(m)F_(2n-m), wherein n is an integer from 2 to 8 and m is an integer from 0 to 2n−1.
 11. The composition according to claim 10 further comprising at least one hydrofluoroalkane having the formula C_(n)H_(m+2)F_(2n-m).
 12. The composition of claim 11, wherein the molar ratio of the hydrofluoroalkane to the fluoroolefin is from 5:1 to 1:1 at the back of the bed.
 13. A composition comprising at least one fluoroolefin having the formula C_(n)H_(m)F_(2n-m); wherein n is an integer from 2 to 8 and m is an integer from 0 to 2n−1; hydrogen (H₂); and a palladium catalyst supported on a carrier comprising α-Al₂O₃.
 14. The composition of claim 13, wherein the palladium catalyst supported on the carrier comprises a bed having a front and a back, wherein the palladium catalyst in the front of the bed has a first palladium concentration lower than a second palladium concentration of the palladium catalyst in the back of the bed.
 15. The composition of claim 13 further comprising at least one hydrofluoroalkane having the formula C_(n)H_(m+2)F_(2n-m).
 16. A process comprising flowing a composition comprising at least one fluoroolefin across a bed of a palladium catalyst supported on a carrier comprising α-Al₂O₃, the bed having a front and a back, the composition flowing from the front of the bed to the back of the bed, wherein the palladium catalyst in the front of the bed has a first palladium concentration lower than a second palladium concentration of the palladium catalyst in the back of the bed, wherein the at least one fluoroolefin has the formula C_(n)H_(m)F_(2n-m), wherein n is an integer from 2 to 8 and m is an integer from 0 to 2n−1.
 17. The process of claim 16, wherein the composition further comprises hydrogen (H₂). 